Masters Varnish Pro Epoxy

Polyurethane Varnish Pro Epoxy - Solvent based
Packaging: Cans of 2 kg
Coverage: 100gr for 1 sqm

Warning : This product is based on solvents. Professionnal use only

  • Gloss
€63.60 (tax incl.) €53.00 (tax excl.)
Tax included
Description

Masters Varnish Pro Epoxy, an epoxy bi-component varnish

It is based on an epoxy resin which forms a waterproof membrane after polymerization. It can be used for protect all decorative concrete, especially for countertop, or where a chemical protection is needed.

How to use ?

1. Preparing surfaces

The surface must be clean, dry and free of dust and other substances such as paint, oil, grease, fluorescence, glue, or old sealers.

If you have any doubts about the cleanliness of the substrate, it is preferable to perform a light sanding with 120 grit.

2. Product preparation

Masters Varnish Pro Epoxy is bi-component product. Component A (resin) and B (hardener) are packed in two separate containers. You need to prepare a mix before using. It's necessary to measure with a scale (weight) one part of the B component for four parts of the A component (Ratio 4/1).
The two components should be mixed, with a low speed mixer (300rpm) during 2 minutes.

Warning: Prepare only the necessary quantity for one coat. Once mixed, the product can not be preserve for a future use.

3. Application

Masters Varnish Pro Epoxy is applied with roller or brush in two coats. Depending on the weather conditions, each layer should be applied at 12 hours interval.
Let it dry during 48 hours before allow traffic.

Data sheet
MVPROEPO
Form
Bi-component
Compositions
Epoxy resin - Solvent based
Coverage
1 kg for 10sqm
VOC's
500gr/l
Effect
Gloss
Colour
Tansparent (light amber)
Properties
Mixing ratio A/B: 4/1
Drying time
To touch: 6 hours - To sand: 24 hours
Pot life
One hour
Shelf life
24 months
Packaging
2 kg
Use
Inside